ES1 Stainless Steel Resists Corrosion and Fatigue
Resource from: ES1 Stainless Steel Likes:3053
Feb 03,2010
NSK has developed ES1 stainless steel for use in high-humidity chemical and hygienic environments, where corrosion can impair the reliable long-term operating life of rolling bearings.
ES1 provides superior corrosion resistance and rolling contact fatigue life to conventional AISI 440C steel in wet and aggressive environments; this helps to reduce maintenance, downtime and replacement-bearing costs.
Until the development of ES1, AISI 440C had been the general choice for use in bearing applications where corrosion resistance was a primary concern.
Because the steel contains coarse eutectic carbides that act as crack initiators under rolling contact stress, the performance of AISI 440C had not always proven satisfactory.
ES1 steel has no eutectic carbides but consists of fine carbides, nitrides and strong martensite, resulting in improved resistance to corrosion and fatigue.
ES1 also has optimum nitrogen content and lower carbon content to suppress the eutectic carbides generated in conventional steel-making processes.
The operating benefits of this new material specification have been proven following extensive testing by NSK.
ES1 outperformed other stainless steels in a five per cent aqueous sodium-chloride immersion test, a salt-water spray test, 5-N sulphuric acid and 5-N hydrochloride solution immersion tests and during life tests in water.
In the aqueous sodium-chloride immersion test, test pieces of ES1, 13Cr stainless steel and AISI 440C were immersed in a five per cent aqueous sodium-chloride solution at room temperature for eight hours.
Before immersion in the solution, all surfaces of the test pieces were polished, then passivation treatment was applied.
The test revealed that the conventional AISI 440C and 13Cr stainless steels rusted, whereas ES1 did not.
Similar results were also recorded in the saltwater spray test, with both AISI 440C and 13Cr rusting considerably, while ES1 did not.
Additional performance advantages were recorded for ES1 in the water-immersion test.
The test bearings were 51305 thrust ball bearings with fluororesin cages and silicon-nitride balls.
They were subjected to a load of 980N (maximum contact pressure: 1470MPa) and rotating speed of 1,000rev/min, until the bearing vibration level reached about five times its initial value.
Under these conditions the test results revealed that ES1 provides approximately five times longer life than AISI 440C.
Because bearings manufactured from stainless steel are routinely exposed to cleaning solutions of sulphuric acid and hydrochloric acid, a further corrosion test was undertaken.
This evaluated the corrosion resistance of ES1, 13Cr stainless steel and AISI 440C in a 5-N aqueous sulphuric-acid solution and 5-N hydrochloric-acid solution.
In the test, samples of each type of steel were immersed in the solutions at room temperature for 20 hours.
The amount of corrosion was then measured.
This revealed that ES1 is superior to both conventional stainless steels in its resistance to both sulphuric and hydrochloric acids.
NSK has developed ES1 stainless steel for use in high-humidity chemical and hygienic environments, where corrosion can impair the reliable long-term operating life of rolling bearings.
ES1 provides superior corrosion resistance and rolling contact fatigue life to conventional AISI 440C steel in wet and aggressive environments; this helps to reduce maintenance, downtime and replacement-bearing costs.
Until the development of ES1, AISI 440C had been the general choice for use in bearing applications where corrosion resistance was a primary concern.
Because the steel contains coarse eutectic carbides that act as crack initiators under rolling contact stress, the performance of AISI 440C had not always proven satisfactory.
ES1 steel has no eutectic carbides but consists of fine carbides, nitrides and strong martensite, resulting in improved resistance to corrosion and fatigue.
ES1 also has optimum nitrogen content and lower carbon content to suppress the eutectic carbides generated in conventional steel-making processes.
The operating benefits of this new material specification have been proven following extensive testing by NSK.
ES1 outperformed other stainless steels in a five per cent aqueous sodium-chloride immersion test, a salt-water spray test, 5-N sulphuric acid and 5-N hydrochloride solution immersion tests and during life tests in water.
In the aqueous sodium-chloride immersion test, test pieces of ES1, 13Cr stainless steel and AISI 440C were immersed in a five per cent aqueous sodium-chloride solution at room temperature for eight hours.
Before immersion in the solution, all surfaces of the test pieces were polished, then passivation treatment was applied.
The test revealed that the conventional AISI 440C and 13Cr stainless steels rusted, whereas ES1 did not.
Similar results were also recorded in the saltwater spray test, with both AISI 440C and 13Cr rusting considerably, while ES1 did not.
Additional performance advantages were recorded for ES1 in the water-immersion test.
The test bearings were 51305 thrust ball bearings with fluororesin cages and silicon-nitride balls.
They were subjected to a load of 980N (maximum contact pressure: 1470MPa) and rotating speed of 1,000rev/min, until the bearing vibration level reached about five times its initial value.
Under these conditions the test results revealed that ES1 provides approximately five times longer life than AISI 440C.
Because bearings manufactured from stainless steel are routinely exposed to cleaning solutions of sulphuric acid and hydrochloric acid, a further corrosion test was undertaken.
This evaluated the corrosion resistance of ES1, 13Cr stainless steel and AISI 440C in a 5-N aqueous sulphuric-acid solution and 5-N hydrochloric-acid solution.
In the test, samples of each type of steel were immersed in the solutions at room temperature for 20 hours.
The amount of corrosion was then measured.
This revealed that ES1 is superior to both conventional stainless steels in its resistance to both sulphuric and hydrochloric acids.
(ES1 Stainless Steel)
【CBCC News Statement】
1.The news above mentioned with detailed source are from internet.We are trying our best to assure they are accurate ,timely and safe so as to let bearing users and sellers read more related info.However, it doesn't mean we agree with any point of view referred in above contents and we are not responsible for the authenticity. If you want to publish the news,please note the source and you will be legally responsible for the news published.
2.All news edited and translated by us are specially noted the source"CBCC".
3.For investors,please be cautious for all news.We don't bear any damage brought by late and inaccurate news.
4.If the news we published involves copyright of yours,just let us know.
1.The news above mentioned with detailed source are from internet.We are trying our best to assure they are accurate ,timely and safe so as to let bearing users and sellers read more related info.However, it doesn't mean we agree with any point of view referred in above contents and we are not responsible for the authenticity. If you want to publish the news,please note the source and you will be legally responsible for the news published.
2.All news edited and translated by us are specially noted the source"CBCC".
3.For investors,please be cautious for all news.We don't bear any damage brought by late and inaccurate news.
4.If the news we published involves copyright of yours,just let us know.
BRIEF INTRODUCTION
Cnbearing is the No.1 bearing inquiry system and information service in China, dedicated to helping all bearing users and sellers throughout the world.
Cnbearing is supported by China National Bearing Industry Association, whose operation online is charged by China Bearing Unisun Tech. Co., Ltd.
China Bearing Unisun Tech. Co., Ltd owns all the rights. Since 2000, over 3,000 companies have been registered and enjoyed the company' s complete skillful service, which ranking many aspects in bearing industry at home and abroad with the most authority practical devices in China.